Dual
wall heat-shrinkable tube
Adopt Flame retardant, cross-linked polyilefin, with an inner
coating of
hot-melt adhesive and an outer layer that shrinks to provide
electrocal and mechanical protection. Insulates and seals a
variety of electrical wirings.
1.Operating Temperature: 45¡æ~125¡æ;
2.Shrink Temperature:Start at 70¡æ; shrunk totally at 120¡æ;
3.Inner layar glue melt temperature: 70¡æ~90¡æ;
4.Shrink ratio:3:1£¬4:1, Longnitudinal Shrink radio¡Ü¡À8%;
5.Waterproof, RoHS compliant.
6.Standard color: Black (Other color available upon request.)
7.Approvals: UL, RoHS |
|
| |
| Technical
Data: |
|
Property
|
Test
Method
|
Stantard
|
| Tensile
Strength(MPa) |
ASTMD
2671
|
¡Ý12
|
| Elongation
at Brealk |
ASTMD
2671
|
¡Ý300
|
| Tensile
Strength after Aging(MPa) |
UL
224
158¡æ¡Á168h
|
¡Ý7.3
|
| Elongation
at Brealk after Aging(%) |
UL
224
158¡æ¡Á168h
|
¡Ý200
|
| Dielectric
strength |
IEC
243
|
¡Ý15
|
| Volume
Resistance |
IEC
93
|
¡Ý1¡Á1014
|
|
|
| |
| Hot
Melting Adhesive Property |
|
Property
|
Test
Method
|
Stantard
|
| Water Absorption |
ASTM-D570
|
<0.2%
|
| Vicat Softening
Point |
ASTM-E8
|
95¡æ
|
| PeelStrength(PE) |
ASTM-D1000
|
120N/25m
|
| PeelStrength(AL) |
ASTM-D1000
|
80N/25m
|
|
| |
|
W-1-SB(3X)
Specification:
|
|
Size
|
As
Supplied(mm)
|
After
Recovered(mm)
|
Stantard
Package
m/spool m/piece
|
Application
range(mm)
|
|
Inch
|
(mm)
|
Min.I.D.
|
Average
W.T.
|
Max.I.D.
|
Total
W.T.
|
Adhesive
thickness
|
Meter/
spool
|
Spools/
carton
|
Carton
Size(cm)
|
| 1/8 |
¦µ3.2 |
¡Ý3.2 |
0.30¡À0.08 |
¡Ü1.00 |
0.95¡À0.08 |
0.35¡À0.08 |
200 |
10 |
46¡Á46¡Á44.5 |
1.0~3.1 |
| 3/16 |
¦µ4.8 |
¡Ý4.8 |
0.46¡À0.08 |
¡Ü1.60 |
1.10¡À0.08 |
0.40¡À0.08 |
100 |
10 |
46¡Á46¡Á44.5 |
1.8~4.6 |
| 1/4 |
¦µ6.4 |
¡Ý6.4 |
0.50¡À0.08 |
¡Ü2.20 |
1.20¡À0.08 |
0.45¡À0.08 |
100 |
6 |
46¡Á46¡Á44.5 |
2.4~6.4 |
| 5/16 |
¦µ7.9 |
¡Ý7.9 |
0.52¡À0.08 |
¡Ü2.70 |
1.35¡À0.08 |
0.50¡À0.08 |
100 |
5 |
46¡Á46¡Á44.5 |
2.9~7.7 |
| 3/8 |
¦µ9.5 |
¡Ý9.5 |
0.55¡À0.08 |
¡Ü3.20 |
1.45¡À0.08 |
0.50¡À0.08 |
Meter/
bag
|
Bags/
carton
|
Carton
Size(cm)
|
3.4~9.4 |
| 61 |
6 |
130¡Á20¡Á16 |
| 1/2 |
¦µ12.7 |
¡Ý12.7 |
0.68¡À0.08 |
¡Ü4.20 |
1.70¡À0.08 |
0.50¡À0.08 |
36.6 |
5 |
130¡Á20¡Á16 |
4.4~12.5 |
| 5/8 |
¦µ15.0 |
¡Ý15.0 |
0.70¡À0.10 |
¡Ü5.20 |
1.80¡À0.10 |
0.55¡À0.10 |
30.5 |
5 |
130¡Á20¡Á16 |
5.4~14.8 |
| 3/4 |
¦µ19.1 |
¡Ý19.1 |
0.76¡À0.10 |
¡Ü6.30 |
2.00¡À0.10 |
0.55¡À0.10 |
30.5 |
6 |
130¡Á20¡Á16 |
6.5~18.8 |
| 1 |
¦µ25.4 |
¡Ý25.4 |
0.78¡À0.10 |
¡Ü8.50 |
2.10¡À0.10 |
0.55¡À0.10 |
30.5 |
5 |
130¡Á20¡Á16 |
8.8~25 |
| 1-1/4 |
¦µ30.0 |
¡Ý30.0 |
0.80¡À0.10 |
¡Ü10.20 |
2.20¡À0.10 |
0.60¡À0.10 |
24.4 |
5 |
130¡Á20¡Á16 |
10.5~30 |
| 1-1/2 |
¦µ39.0 |
¡Ý39 |
0.85¡À0.10 |
¡Ü13.50 |
2.40¡À0.10 |
0.60¡À0.10 |
18.3 |
5 |
130¡Á20¡Á16 |
14.0~39 |
| 2 |
¦µ50.0 |
¡Ý50 |
0.95¡À0.10 |
¡Ü17.00 |
2.70¡À0.10 |
0.70¡À0.10 |
12.2 |
5 |
130¡Á20¡Á16 |
17.5~49 |
| 5/2 |
¦µ64 |
¡Ý64 |
0.95¡À0.10 |
¡Ü21.00 |
3.00¡À0.15 |
0.70¡À0.10 |
6.1 |
7 |
130¡Á20¡Á16 |
22~62 |
| 3 |
¦µ75 |
¡Ý76 |
1.00¡À0.15 |
¡Ü25.00 |
3.20¡À0.15 |
1.00¡À0.15 |
1.22 |
¡ª¡ª |
130¡Á20¡Á16 |
26~72 |
| 7/2 |
¦µ90 |
¡Ý90 |
1.00¡À0.15 |
¡Ü30.00 |
3.30¡À0.15 |
1.00¡À0.15 |
1.22 |
¡ª¡ª |
130¡Á40¡Á16 |
32~88 |
| 4 |
¦µ100 |
¡Ý100 |
1.20¡À0.15 |
¡Ü34.00 |
3.50¡À0.15 |
1.20¡À0.15 |
1.22 |
¡ª¡ª |
130¡Á40¡Á16 |
36~90 |
| 5 |
¦µ125 |
¡Ý125 |
1.20¡À0.15 |
¡Ü42.00 |
3.50¡À0.15 |
1.20¡À0.15 |
1.22 |
¡ª¡ª |
130¡Á40¡Á16 |
44~125 |
|
|
| |
|
W-1-SB(4X)
Specification:
|
|
Size
|
As
Supplied Min.I.D.
|
After
Recovered(mm)
|
Stantard
Package
m/spool or
m/pc
|
|
mm
|
inch
|
Max.I.D.
|
Total
W.T.
|
Adhesive
thickness
|
|
¦µ4.0
|
¡ª¡ª
|
4.0
|
1.0
|
1.0¡À0.15
|
0.4¡À0.15
|
200
|
|
¦µ6.0
|
¡ª¡ª
|
6.0
|
1.5
|
1.1¡À0.15
|
0.4¡À0.15
|
100
|
|
¦µ8.0
|
¡ª¡ª
|
8.0
|
2.0
|
1.5¡À0.15
|
0.5¡À0.15
|
50
|
|
¦µ12.0
|
¡ª¡ª
|
12.0
|
3.0
|
1.7¡À0.15
|
0.5¡À0.15
|
1.22
|
|
¦µ16.0
|
¡ª¡ª
|
16.0
|
4.0
|
2.0¡À0.15
|
0.6¡À0.15
|
1.22
|
|
¦µ20.0
|
¡ª¡ª
|
20.0
|
5.0
|
2.3¡À0.25
|
0.6¡À0.15
|
1.22
|
|
¦µ24.0
|
¡ª¡ª
|
24.0
|
6.0
|
2.5¡À0.25
|
0.6¡À0.15
|
1.22
|
|
¦µ32.0
|
¡ª¡ª
|
32.0
|
8.0
|
2.8¡À0.30
|
0.7¡À0.15
|
1.22
|
|
¦µ52.0
|
¡ª¡ª
|
52.0
|
13
|
3.0¡À0.30
|
0.7¡À0.15
|
1.22
|
|
|
| |